Fiberon™ PA6-CF20
Fiberon™ PA6-CF20 - 1.75mm (Old Packaging) / 0.5kg / Black is backordered and will ship as soon as it is back in stock.
Couldn't load pickup availability
Description
Description
Fiberon™ PA6-CF20 is a carbon fiber reinforced PA6 (Nylon 6) filament. The carbon fiber reinforcement provides significantly improved stiffness, strength and heat resistance with outstanding layer adhesion.
Fiberon™ PA6-CF20 is the same great formula as PolyMide PA6-CF, although Fiberon™ PA6-CF20 may print in a slightly darker black shade color than its predecessor.
Download the TDS to learn more about the performance of the material.
Printing Temperature: 280˚C - 300˚C
Build Plate Temperature: 40˚C - 50˚C
Chamber Temperature: Room Temperature
Printing Speed: up to 300mm/s
Cooling Fan: OFF
Direct Drive:
Retraction Distance: 3mm
Retraction Speed: 40mm/s
Indirect Drive:
Retraction Distance: 6mm
Retraction Speed: 60mm/s
Recommended Drying Settings:
Regular Oven: 100˚C for 10h
PolyDryer: Level 3 for 18h (PolyDryer™)
(Only if the material has absorbed moisture)
Annealing Settings: 100˚ for 16h
Content
0.5kg cardboard spool:
Spool Inner Hole Diameter: 55±1mm
Spool Diameter: 200±1mm
Spool Width: 65.6±2mm
Spool Weight: 190±7g
0.75kg cardboard spool:
Spool Inner Hole Diameter: 55±1mm
Spool Diameter: 200±1mm
Spool Width: 50.6±2mm
Spool Weight: 125±7g
1kg cardboard spool:
Spool Inner Hole Diameter: 55±1mm
Spool Diameter: 200±1mm
Spool Width: 65.6±2mm
Spool Weight: 140±7g
2kg cardboard spool:
Spool Inner Hole Diameter: 55±1mm
Spool Diameter: 250±1mm
Spool Width: 117.2±2mm
Spool Weight: 370±18.5g
3kg cardboard spool:
Spool Inner Hole Diameter: 55±1mm
Spool Diameter: 250±1mm
Spool Width: 117.2±2mm
Spool Weight: 425±21.3g
5kg plastic spool: 32mm/300mm/160mm/819g
Spool Inner Hole Diameter: 32±1mm
Spool Diameter: 300±1mm
Spool Width: 160±1mm
Spool Weight: 819±30g
Spool Material: PP
Payment & Security
Payment methods
Your payment information is processed securely. We do not store credit card details nor have access to your credit card information.